Experimental Determination of Interfacial Energies for Solid Sn in Equilibrium with Sn-Mg-Zn Liquid
Özet
The equilibrated grain boundary groove shapes of solid Sn in equilibrium with Sn-Mg-Zn liquid were observed
from a quenched sample by using a radial heat flow apparatus. The Gibbs-Thomson coefficient, solid-liquid
interfacial energy and grain boundary energy of solid Sn were determined from the observed grain boundary
groove shapes. The thermal conductivity of the eutectic solid phase for Sn-8.12 at% Mg-4.97 at% Zn alloy and the
thermal conductivity ratio of the liquid phase to the solid phase for Sn-8.12 at% Mg-4.97 at% Zn alloy at eutectic temperature were also measured with a radial heat flow apparatus and a Bridgman-type growth apparatus,
respectively. The Gibbs-Thomson coefficient, solid-liquid interfacial energy and grain boundary energy of solid
Sn in equilibrium with Sn-Mg-Zn liquid were determined to be (8.3 ± 0.6)×10-8 Km, (118.5 ± 14.2)×10-3 J m-2
and (225.1 ± 29.3)×10-3 J m-2 respectively from observed grain boundary groove shapes. A comparison of
present results for solid Sn in the Sn-8.12 at% Mg-4.97 at% Zn alloy with the results obtained in previous works
for similar solid Sn in equilibrium with different binary or ternary liquid was made.